Super Translucent Zirconia Block Zirkonzahn Cadcam M5 Suitable Ice & Prettau Zirconium Blank Dental Lab Equipment Supplier

Super Translucent Zirconia Block Zirkonzahn Cadcam M5 Suitable Ice & Prettau Zirconium Blank Dental Lab Equipment Supplier

Basic Info Thriden zirconia block is presintered 3mol% yttria (Y2O3) stabilized zirconia (ZrO2) block, which is made from the finest nano zirconia powder by dry and cold isostatic pressing and machining. CNC dental solution high translucent zirconia(or called Ice) is used for copings or in...
Product description

Super Translucent Zirconia Block Zirkonzahn Cadcam M5 Suitable Ice & Prettau Zirconium Blank Dental Lab Equipment Supplier

Model NO.:TDZ0095 Material:Zirconia, Titanium, PMMA, Wax, Co-Cr, Nicr, Resin
3-Point Bending Strength:1200-/+50MPa, 3-Point Bending Strength, Cold Isost Thickness:10/12/14/16/18/20/22/25mm, White, Preshaded, Multil
Sintering Dentsity:6.07-6.09g/cm3 Sintering Dentsity, 2.5ug*Cm2 Chemic Application:Crown, Coping, Bridge, Full Contour, Inlays, Onlays, V
Certification:CE, FDA, ISO 13356, 100% Compatible, 100% Biocompat Raw Material:Fine Nano Zirconia Powder, Resin Wax, Titanium, Nicr
Products:Dental CAD Cam Material, Milling Bur, Sintering Fu Transparency:High Translucent, Super Translucent, Strength, Ice
Compatible:Amann Girrbach, Wieland, Roland, VHF, Imes-Icores, Orig


Thriden zirconia block is presintered 3mol% yttria (Y2O3) stabilized zirconia (ZrO2) block, which is made from the finest nano zirconia powder by dry and cold isostatic pressing and machining.
CNC dental solution high translucent zirconia(or called Ice) is used for copings or in restorations, translucent is more than 30%.
CNC dental solution super translucent zirconia (or called Prettau) is used for full contour or full solid zirconia crown, copping or bridge in the aesthetic zone, translucent can be more than 40%.
Blocks are 100% suitable with all open cadcam milling system including Roland, Wieland, Imes-icores, VHF, Yenadent and so on.
 
Finest powder: Easy to cut, no porcelain breakage, less scraps, excellent biocompatibility and aesthetics. 
Dry and cold isostatic pressing: fully densify,  uniform lifetime compressive strength,
Scaling factor: carefully determined in each batch persistent and consistency,
Coloring: imagination permeability coloring not only stay on surface.
Package: each block in one box
Thickness:  OD95*10mm --25mm
 
technical parameter


Colour

White(light colored)and uniform, thin-wall is semitransparent

Sintering density
(densely sintered in high temperature)

(6.05±0.03) g/cm3    

Chemical compositions

ZrO2+HfO2+Y2O3>99.0 wt%
Al2O3<O.5 wt%
Other oxides<O.5 wt%

Pre-sintering Density

&#8805; 2.95g/cm3

Post-sintering Hardness

Hv10 &#8805; 12.5Gpa

Post-sintering Flexural Strength:

> 1100Mpa

Sintering Shrinkage

19% - 22%

Pre-sintering Solubility

&#8804; 2000&#181;g&#183;cm-2

Post-sintering Solubility:

&#8804; 100&#181;g&#183;cm-2

Post-sintering Flexural Strength:

> 1100Mpa

Chemical solubility

6.7&#181;g&#183;cm-2

Radio activity uranium-238 per unit mass:

&#8804; 0.02Bq&#183;g-1

Cytotoxicity

0

Short term systemic toxicity test -oral route

no systemic toxicity

Delayed-type hypersensitivity

no sensitization

Hemolysis

0

 

Dingding Titanium is one of the leading China Latest Titanium Products manufacturers and suppliers, equipped with a productive super translucent zirconia block zirkonzahn cadcam m5 suitable ice & prettau zirconium blank dental lab equipment supplier factory and company, welcome to import good products from us.